This article reports on a study that examined the coating effects on mid-infrared reflection spectra of fabrics.
Polymer films of varying thicknesses were deposited onto cotton and polyester fabric samples by dip-coating from solution. Scanning electron microscopy (SEM) images of the coated fabric samples were used to evaluate the quality of the polymer coating. The samples were analyzed by infrared diffuse reflection spectroscopy to determine the relationship between film thickness and the effect of the coating on the spectroscopy of the two fabrics. Effects observed in four limiting cases were examined: (Case I) weak coating absorption on a fabric with weak absorption at the same frequency; (Case II) strong coating absorption in a spectral region of weak fabric absorption; (Case III) weak coating absorption in a spectral region of strong fabric absorption; and (Case IV) strong coating absorption in a spectral region of strong fabric absorption. In the first case, effects were dominated by reduced scattering as the coating is added. In the second case, the strong coating absorption that was observed at low coverages plateaus at higher coverage due to depth of penetration effects. In the third and fourth cases, reduced Fresnel diffuse reflection is measured as the coating is added, consistent with the reduction of scattering observed in the first case. (publisher abstract modified)
Downloads
Similar Publications
- Determining the Precision of High-Throughput Sequencing and Its Influence on Aptamer Selection
- Criticality of Spray Solvent Choice on the Performance of Next Generation, Spray-Based Ambient Mass Spectrometric Ionization Sources: A Case Study Based on Synthetic Cannabinoid Forensic Evidence
- Solving Cases of Sudden Unexpected Natural Death in the Young through Comprehensive Postmortem Genetic Testing